Tunnel magnetoresistance read head with narrow shield-to-shield spacing

ABSTRACT

A tunnel magnetoresistance (TMR) read sensor having a tabbed AFM layer and an extended pinned layer and methods for making the same are provided. The TMR read sensor has an AFM layer recessed from the air bearing surface, providing a reduced shield-to-shield distance.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a divisional of U.S. patent application Ser. No. 14/242,717, filed on Apr. 1, 2014, which is a divisional of and claims priority to U.S. patent application Ser. No. 13/538,650 filed on Jun. 29, 2012, issued as U.S. Pat. No. 8,711,528, which are hereby incorporated by reference.

TECHNICAL FIELD

This invention relates to the field of disk read/write heads and more specifically, to tunnel magnetoresistance (TMR) read heads and method of fabricating the same.

BACKGROUND

Increasing magnetic recording density requires narrower-track widths and narrower shield-to-shield spacing on read heads. Current tunnel magnetoresistance (TMR) read heads comprise a pinned layer coupled to an antiferromagnet (AFM) layer. The TMR read heads further comprise a free layer separated from the pinned layer by a barrier layer. Current attempts to narrow the shield-to-shield spacing by removing the AFM layer have been unsuccessful because AFM-free TMR read heads are prevalently magnetically bi-directional

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention is illustrated by way of example, and not limitation, in the figures of the accompanying drawings in which:

FIG. 1 illustrates a read sensor having a tabbed antiferromagnet (AFM) layer and extended pinned layer.

FIGS. 2A-E illustrate a process for manufacturing a read sensor having a tabbed AFM layer and extended pinned layer.

FIGS. 3A-E illustrate a second process for manufacturing a read sensor having a tabbed AFM layer and extended pinned layer.

DETAILED DESCRIPTION

In the following description, numerous specific details are set forth, such as examples of specific layer compositions and properties, to provide a thorough understanding of various embodiment of the present invention. It will be apparent however, to one skilled in the art that these specific details need not be employed to practice various embodiments of the present invention. In other instances, well known components or methods have not been described in detail to avoid unnecessarily obscuring various embodiments of the present invention.

The terms “over,” “under,” “between,” and “on” as used herein refer to a relative position of one media layer with respect to other layers. As such, for example, one layer disposed over or under another layer may be directly in contact with the other layer or may have one or more intervening layers. Moreover, one layer disposed between two layers may be directly in contact with the two layers or may have one or more intervening layers. In contrast, a first layer “on” a second layer is in contact with that second layer. Additionally, the relative position of one layer with respect to other layers is provided assuming operations are performed relative to a substrate without consideration of the absolute orientation of the substrate.

FIG. 1 illustrates a tunnel magnetoresistance (TMR) read sensor having a tabbed AFM layer and an extended pinned layer. The read sensor has an air-bearing surface plane (ABS) 104 and a plurality of layers perpendicular to the ABS 104. A shield layer 116 is disposed over a substrate. The shield layer 116 comprises NiFe or another conventional magnetic shield material for TMR read sensors. In some cases, the shield layer 116 is composed of a single shield material. In other cases, the shield layer 116 has a composite structure. For example, shield layer 116 may comprise on or more layers of NiFe, NiFe multilayers, CoFe, or Ru. A top shield 101 is disposed over the TMR read sensor layers. The top shield layer 101 may also comprise NiFe or other conventional material for TMR read sensors. For example, the top shield 101 may have a composition similar to the lower shield layer 116. The shield-to-shield distance 117 is the distance between the first shield layer 116 and the top layer 101 at the ABS 104.

A seed layer 115 is disposed on the shield layer 116. The seed layer may comprise Ta, Ru, a Ta/Ru bilayer or other conventional seed layers. An antiferromagnetic layer 113 (AFM layer) is disposed over the shield layer 116 on the seed layer 115. An antiferromagnet exchange biased pinned layer 114 (or “stitching layer”) is disposed over the AFM layer 113. The AFM layer 113 and stitching layer 114 are recessed from the ABS 104 by a recess distance 112. Because the AFM layer 113 and stitching layer 114 are recessed from the ABS, the layers do not contribute to the shield-to-shield distance 117. In particular cases, the recess distance may be between 10 and 500 nm.

The AFM material layer 113 may comprise various antiferromagnetic materials, such as IrMn, PtMn, PdMn, NiMn, RhMn, or RhRuMn. IrMn is often used in TMR AFM layers because it provides a thinner AFM layer than other materials. Because the AFM layer 113 is recessed 112 from the ABS 104, thicker AFM layers 113 may be employed than in conventional TMR sensors without increasing shield-to-shield distance 117. Accordingly, other antiferromagnetic materials besides IrMn may be used without increasing shield-to-shield distance 117.

The stitching layer 114 is magnetically pinned by the AFM layer 113 in a direction 120. In the illustrated sensor, the stitching layer 114 comprises a layer of CoFe that provides a material transition between the AFM material layer 113 and the pinned layer 108. In other cases, the stitching layer 114 comprises a tri-layer of a first layer of a soft magnetic material such as CoFe, a second layer of Ru, Cr, Ag, or Au, or other suitable non-magnetic material, and a third layer of the soft magnetic material, such as CoFe. The non-magnetic material may a thickness approximately equal to the first or second oscillatory peak of the exchange coupling between the two soft magnetic layer of the multilayer. These thicknesses increase the pinning strength provided by the layer 114. For example, for a CoFe/Ru/CoFe multilayer stitching layer 114, the Ru thickness is either approximately 4.3 Å for the first oscillatory peak or between approximately 7 and 8 Å for the second oscillatory peak. In some cases, the stitching layer 114 may be omitted without impacting the coupling between the AFM layer 113 and the pinned layer 108.

A second pinned layer 108 is disposed on the antiferromagnet exchange biased pinned layer 114 along its area and on the seed layer 115 along the shield 116 contact area. The second pinned layer 108 has its magnetic direction fixed by the stitching layer 120. The second pinned layer 108 extends from the ABS 104 to the rear edge of the first pinned layer 114. The pinned layer 108 may comprise conventional pinned layer materials. For example, the pinned layer 108 may have a composite, multilayer structure including a first ferromagnetic layer 110, a non-magnetic layer 109, and a second ferromagnetic layer 107. The ferromagnetic layers 110 and 107 pinned layer 108 may be composed of conventional ferromagnetic materials such as NiFe, CoFe, or CoNiFe. The non-magnetic layer 109 may be composed of conventional non-magnetic materials, such as Ru. In the illustrated sensor, the first and second ferromagnetic layers 107, 110 are in an anti-parallel configuration 118, 119, which is fixed by the orientation 120 of the first pinned layer 114.

The TMR read sensor further comprises a free layer 105 separated from the pinned layer 108 by a barrier layer 106 and separated from the top shield layer 101 by a capping layer 121. The barrier layer 106, the capping layer 121, and free layer 105 extend from the ABS 104 to a stripe height distance 102. In some cases, the recess distance 112 is greater than or equal to the stripe height distance 102. In other cases, the recess distance 112 is less than the stripe height distance. The free layer 105 comprises a ferromagnetic material, such as NiFe, CoFe, or CoNiFe. The barrier layer comprises an insulating material, and may be selected to provide a seed layer for the free layer 105. For example, MgO may be used as the barrier layer 106. The capping layer 121 isolates the free layer 105 from the shield layer 101 and comprises a non-magnetic material, such as Ru, Ta, or a bilayer thereof.

A region of conventional insulating substrate material, such as AlOx 103 covers the rear portion of the pinned layer 108 and back of the stitching layer 114 and AFM layer 113. Along with the free layer 105, the material layer 103 provides a planar surface for a shield layer 101. As discussed above, this may comprise NiFe or other conventional material for TMR read sensors.

FIGS. 2A-2E illustrate a first process for making a TMR read head.

The first processing step is illustrated in FIG. 2A. Here, a shield layer 203 is provided on a substrate. A seed layer for the TMR read sensor is deposited on the shield layer 203. In some embodiments, the shield layer 203 may have a composite structure. For example, the shield layer 203 may comprise one or more alternating layers of magnetic shield material and seed layers. The layers of magnetic shield materials may comprise conventional shield materials, such as NiFe. The seed layers may comprise a material that mimic the crystal structure of the magnetic shield materials, such as a layer of CoFeB. Alternatively, the seed layer may comprise an amorphous structure that isolates the grain structure of alternating shield material layers. The TMR seed further comprises a seed layer or layers 202, 201 for the pinned layer. For example, a bilayer of tantalum 202 and ruthenium 201 may be provided as a seed for the pinned layer. As discussed below, a further process step involves cleaning the assembly by material, so the uppermost layer 201 of the seed layer is sufficiently thick so that a proper thickness remains after planarization. In a particular case, the Ta layer 202 may be 10 nm thick and the Ru layer 201 may be 60 nm thick.

FIG. 2B illustrates a second process step of the first method for making a TMR read head. In this process step a layer of photoresist 206 is formed on the substrate assembly. The photoresist pattern 206 is configured for formation of a region for the AFM layer that is recessed from the ABS.

FIG. 2C illustrates a third process step of the first method for making a TMR read head. Here, the substrate assembly is etched to form a region for the AFM and the AFM is deposited in the region. The step of etching comprises etching through the seed layers 201, 202 into the shield layer 203. The depth of penetration into the shield layer is configured according to the desired height of the AFM layer. After deposition, the photoresist pattern 206 is removed. In the illustrated method, the AFM includes an AFM seed layer 210, 209. The AFM seed layer 210, 209 comprises a bilayer of Ta 210 and Ru 209. An AFM material layer 208 is deposited on the seed layer 209, 210. Then, a soft magnetic stitching layer 207 is deposited on the AFM material layer 208. Similar to the thickness of the upper seed layer 201, the thickness for the stitching layer 207 is configured according to the amount of material removal to occur during the subsequent cleaning step.

In a particular case, the first seed layer may comprise 10 nm of Ta, the second seed layer may comprise 10 nm of Ru, the AFM material layer may comprise 80 nm of IrMn, and the stitching layer may comprise 100 nm of CoFe. In this case, the depth of penetration into the shield layer 203 is 130 nm.

FIG. 2D illustrates a fourth process step of the first method for making a TMR read head. In this process step, the pinned layer, free layer, and attendant layers are deposited on the substrate assembly. First, the upper layers of the assembly are cleaned by removal of some of the material of the layers—for example, by sputter each clean removal of 50 nm of material. After cleaning, the first magnetic layer 211, the non-magnetic layer 212, and the second magnetic layer 213 are sequentially deposited. The seed layer 216 is then deposited on the second magnetic layer 213. The free layer 215 is deposited on the seed layer 216. Then, the capping layer 217 is deposited on the free layer.

In some cases, after the capping layer 217 is deposited, the assembly is magnetically annealed. Additionally, the manufacture of the assembly up to FIG. 2C may be performed in situ or ex situ with the completion of the assembly in FIG. 2D.

FIG. 2E illustrates a fifth process step of the first method for making the TMR read head. After the deposition of the head layers up to the capping layer 217, conventional subsequent processing is performed on the assembly to define the stripe height and track width. During these subsequent processing steps, the free layer 215, capping layer 217, and seed layer 216 are etched to the proper profile for the track width and stripe height. A filling material 214, such as AlOx is deposited on the substrate to provide a planar region for the upper shield layer 218. Finally, the upper shield layer 218 is deposited on the substrate.

FIGS. 3A-3E illustrate a second method for making a TMR read head.

FIG. 3A illustrates a first process step of the second method of making a TMR read head. The second method begins by depositing the AFM layer on the shield 305. Similar to FIG. 2C, the AFM layer comprises a seed layer 304, 303, such as a Ta/Ru bilayer, an AFM material layer 302 and a soft stitching layer 301. The AFM layer is deposited with similar thicknesses as the AFM layer in FIG. 2C. For example, in a particular case, the AFM film stack comprises 10 nm of Ta 304, 10 nm of Ru 303, 80 nm of IrMn, and 100 nm of CoFe.

FIG. 3B illustrates a second process step of the second method of making a TMR read head. In this method, a photoresist pattern 306 is formed on the upper layer 301 of the AFM layer. The photoresist pattern 306 is configured to provide a region for formation of a TMR read head seed layer such that the remaining AFM layer is recessed from the ABS.

FIG. 3C illustrates a third process step of the second method of making a TMR read head. In this step, the assembly is etched to a predetermined depth into the shield 305. A layer of shield material 309 is deposited in the region to a thickness such that the shield material layer 309 is as thick as that in the second method. A TMR seed bi-layer 308, 307 is then deposited on the shield material layer 309. In some cases, a seed layer, such as a CoFeB layer is deposited on the shield layer 309 prior to the deposition of the shield material layer 209. As with the first method, the second seed layer 307 has a thickness configured for etch cleaning.

In a particular case, the TMR seed layer comprises 150 nm of NiFe, 10 nm of Ta and 60 nm of Ru.

FIG. 3D illustrates a fourth process step of the second method of making a TMR read head. The fourth process step proceeds similarly to the fourth process step of the first method. Like the fourth process step of the first method, this process can be performed in situ or ex situ with the third process step. An etch cleaning step removes a certain thickness of material from the uppermost layers—for example, 50 nm. Next, a pinned layer comprising a first ferromagnetic layer 310 and a second ferromagnetic layer 312 sandwiching a non-magnetic layer 311 is deposited on the substrate assembly after cleaning. Afterwards, a seed layer 313, free layer 315 and capping layer 134 are deposited on the pinned layer. In some cases, the assembly is then magnetically annealed.

As in the first method, after the capping layer 314 is deposited, the assembly may be magnetically annealed. Additionally, the manufacture of the assembly up to FIG. 3C may be performed in situ or ex situ with the completion of the assembly in FIG. 3D.

FIG. 3E illustrates a fifth process step of the second method of making a TMR read head. This process proceeds in a substantially similar manner as described above with respect to FIG. 2E. After the track height and stripe width of the free layer 315 are defined, a filling material 316 is deposited to form a planar region with the capping layer 314 and a top shield layer 317 are deposited on layers 314 and 316.

In the foregoing specification, embodiments of the invention have been described with reference to specific exemplary features thereof. It will, however, be evident that various modifications and changes may be made thereto without departing from the broader spirit and scope of the invention as set forth in the appended claims. The specification and figures are, accordingly, to be regarded in an illustrative rather than a restrictive sense. 

What is claimed is:
 1. A method, comprising: obtaining a substrate comprising a shield layer; depositing an antiferromagnetic layer over the shield layer depositing an antiferromagnet exchange biased pinned layer over the antiferromagnetic layer; forming a photoresist pattern on the antiferromagnet exchange biased pinned layer for a read sensor seed layer deposition; etching the antiferromagnet exchange biased first pinned layer, the antiferromagnetic layer, and a portion of the shield layer to form a region for the read sensor seed layer deposition, the region located such that the remaining antiferromagnet exchange biased first pinned layer and antiferromagnetic layer are recessed from an air bearing surface plane; and depositing the read sensor seed layer in the region.
 2. The method of claim 1, further comprising: etching the substrate for surface planarization after depositing the read sensor seed layer in the region; depositing a second pinned layer over the remaining antiferromagnet exchange biased first pinned layer and the read sensor seed layer intersecting the air bearing surface plane; depositing a barrier layer over the second pinned layer and intersecting the air bearing surface plane; depositing a free layer over the barrier layer and intersecting the air bearing surface plane; and depositing a capping layer over the free layer and intersecting the air bearing surface plane.
 3. The method of claim 1, wherein the steps of etching the antiferromagnet exchange biased first pinned layer to form a region for the read sensor seed layer deposition and depositing the read sensor seed layer are performed in situ.
 4. The method of claim 1, wherein the steps of etching the antiferromagnet exchange biased first pinned layer, the antiferromagnetic layer, and a portion of the shield layer and depositing the read sensor seed layer are performed ex situ.
 5. The method of claim 1, wherein the step of depositing the antiferromagnet exchange biased first pinned layer comprises: depositing a first soft ferromagnetic layer over the antiferromagnetic layer; depositing a non-magnetic layer over the first soft ferromagnetic layer; and depositing a second soft ferromagnetic layer over the non-magnetic layer; and the non-magnetic layer having a thickness approximately equal to a first or a second oscillatory peak of the exchange coupling between the first soft ferromagnetic layer and the second soft ferromagnetic layer; and the non-magnetic layer comprising Ru, Cr, Ag, or Au.
 6. The method of claim 1, further comprising magnetically annealing the assembly formed after the step of depositing the capping layer. 